Hollow Glass Micro Spheres

See Larger Picture : Hollow Glass Micro Spheres

Price
US$ 6.5
Min Order Quantity 100kg / kg
Delivery Lead Time within 10 days
  • Share to :
  • Pinterest
Contact Now* Send an Inquiry to this supplier.
or
Start Order * Name your price

Browse by Category

Contact us

Jinan Great Material Co.,Ltd
[China]

Address
44,wenhuaxi road Jinan Shandong
Phone
86-531-88580380
Contact name
Li Gang

Quick Information

  • Brand Name: great
  • Place of Origin: China
  • Model Number : 70182000

Description

Unique performance 

 

High-performance hollow glass microsphere is a kind of ultra-lightweight inorganic non metallic powder with hollow microsphere, and it is a versatile and high performance new 

lightweight material developed in recent years. It will be the new composite mainstream 

materials at 21 century. 

Its true density is 0.15-0.60g/cm3 with 2-130μm in diameter. It owns features with light weight, large bulky, 

low thermal conductivity, high compressive strength, smoothly mobility. 

It can be used in paint, rubber, plastics, FRP, artificial stone, putty and other products

 as filler and weight-reducing agent. 

It can also be the excellent sensitizer for emulsion explosives; 

 

Because of its high compressive properties, it can be used to produce high-strength low-density cement slurry and low density drilling fluid in oil and gas extraction industry.    

 

Series  of  Products

 

Type

Color

Diameter(um)

Density(g/cm3)

Pressure(Mpa)

T20

white

2-120

0.20

3-4

T25

white

2-110

0.25

5-7

T32

white

2-90

0.32

12-15

T40

white

2-85

0.40

28-33

T46

white

2-80

0.46

38-42

T60

white

8-65

0.60

>60

 

Floating Rate:  >94%

Melting Point:  625°C

PH:           7-8

Component:  Soda Lime Borosilicate Glass

Thermal Conductivity:  0.03~0.06w/m.k     

 

Applications 

Its applications are in the fields of thermal insulation coating, putty, plastic casting polyester,

 FRP, SMC, radome, synthetic foam board, adhesives, printed circuit board substrate, RTM, 

bowling, fan blades, emulsion explosives, golf, sealant, pipeline insulation materials, artificial 

marble, low density oil drilling, light cement, and other deep-sea buoy etc. 

 

Why should we choose Hollow Glass Microspheres? 

Improve flow properties 

Hollow glass microsphere is a tiny sphere with high ball-type rate. Its ball-bearing effect can improve its mobility and reduce the viscosity and internal stress of resin 

mixture. Therefore, during processing, less heat is produced in composite materials so as to 

prevent inadequate lubrication and partial thermal decomposition. It is more likely to extrude

 when molding, which can not only reduce defects in products, but also improve the production 

efficiency by 15% -20%. 

 

A superior substitute of resin 

Hollow glass microspheres occupy less surface area, low oil absorption rate, and evenly 

disperse in mixture. Its easy compression and integration permit high filler loadings. It 

significantly reduces the consumption of resins, increases the amount of filler, and effectively 

reduces VOC indicators, and costs as well. 

Low shrinkage and warpage 

Hollow glass microspheres have the feature of isotropism and high-filling, hence the dimensional stability of the product will be very high and it will reduce the 

shrinkage and warpage. With an appropriate filling ratio, the toughness of the products,

 impact-resistance and surface hardness can be significantly improved. 

More economical 

The density of high-performance hollow glass microspheres is only a fraction of that of the resin. A small amount

 of hollow glass microspheres will be able to replace heavier materials. When considering the 

cost per unit volume, rather than cost per unit weight, high  performance hollow glass

 microspheres can significantly reduce costs. 

Adjusting product density 

 

The density of hollow glass microspheres is usually 0.20 ~ 0.60g/cm3, and the density of 

mineral filler is generally around 2.7 ~ 4.4 g/cm3 (The data adopted is the true particle density).

 In order to obtain the equal size, 14 kilograms or more of talc must be used to obtain the 

same effect of 1 kg of hollow glass microsphere. Hence the desired ideal density can be 

obtained by adding appropriate proportions of hollow glass microspheres. 


Price

  • Price Condition : EXW
  • Price : USD6.5 / kg

Packaging & Delivery

  • Delivery Lead Time : within 10 days
  • Minimum Order : 100kg

Product Image

  • Hollow Glass Micro Spheres image

Send an Inquiry to this supplier

Send an Inquiry to this supplier
* From
  To Li Gang
Jinan Great Material Co.,Ltd
* Buying Product
- Please enter your specific buying item.
e.g. 42 inch LCD TV, leather executive chair
Category : Beads
* Message

Use English only Max. 2000 characters. (Min. 20)

Send